The MARISEAL AQUA PRIMER is mainly used as a primer for polyurethane waterproofing coatings, polyurethane joint sealants and polyurethane and epoxy floor coatings on non-absorbent surfaces like:
It can also be used as a primer on absorbent surfaces like concrete, mortar, plaster, etc.
It can also be used on moist concrete surfaces.
It is also used as a tack-coat between coating layers it intercoating time intervals are overstepped.
100 – 200 gr/m2 in one or two layers.
This coverage is based on practical application by roller onto a smooth surface in optimum conditions. Factors like surface porosity, temperature, humidity, application method and finish required can alter consumption.
The MARISEAL AQUA PRIMER is supplied transparent
Technical dataPROPERTY RESULTS TEST METHOD Composition Epoxy resin + Hardener. Water based Mixing Ratio A : B = 3 : 1 Adhesion to aluminium >2 N/mm2 ASTM D 903 Adhesion to moist concrete (6%) >1,5 N/mm2(concrete failure) ASTM D 903 Hardness (SHORE A Scale) >95 ASTM D 2240 Resistance to Water Pressure No Leak (1m water column, 24h) DIN EN 1928 Service Temperature -30C to +90C Inhouse lab Application Temperature 10C to 35C Conditions: 20C, 50% RH Pot Life 45-50 min Conditions: 20C, 50% RH Overcoating time 6-12 hours Conditions: 20C, 50% RH Final Curing time 7 days Conditions: 20C, 50% RH
The surface needs to be clean, dry and sound, free of any contamination, which may harmfully affect the adhesion of the membrane. Maximum moisture content should not exceed 5%. Substrate compressive strength should be at least 25MPa, cohesive bond strength at least 1.5MPa. New concrete structures need to dry for at least 28 days. Old, loose coatings, dirt, fats, oils, organic substances and dust need to be removed by a grinding machine. Possible surface irregularities need to be smoothened. Any loose surface pieces and grinding dust need to be thoroughly removed.
WARNING: Do not use a metal-ball blasting machine to grind the surface, because the heavy metal-ball impacts destroy the cohesion of the concrete surface and lower its stability.
MARISEAL AQUA-PRIMER Component A and Component B should be mixed by low speed mechanical stirrer, according to the stipulated mixing ratio, for about 3-5 min.
ATTENTION: The mixing of the components has to be effected very thoroughly, especially on the walls and bottom of the pail until the mixture becomes fully homogeneous.
Dilute mixture with 15-25% of clean water, to regulate viscosity.
For best results, the temperature during application and cure should be between 5oC and 35OC. Low temperatures retard cure, while high temperature speed up curing. High humidity may affect the final finish.
Apply the MARISEAL AQUA-PRIMER (diluted with 15-25% clean water) by roller or brush, until the surface is covered.
After approx. 6-12 hours (not later than 24 hours) and while the primer is still a bit tacky, apply the polyurethane coating or the polyurethane joint-sealant.
RECOMMENDATION: If the surface is very brittle, like lightweight concrete or porous cement screed, apply two layers of the MARISEAL AQUA PRIMER.
ATTENTION: Please ensure consumption within the Pot Life.
WARNING: Do not apply the MARISEAL AQUA PRIMER, at ambient and ground temperatures under 10C.
MARISEAL AQUA PRIMER is supplied in 15+5kg and 3+1kg pails. Pails should be stored in dry and cool rooms for upto9months. Protect the material against moisture and direct sunlight. Storage temperature: 5-30C. Products should remain in their original, unopened containers, bearing the manufacturers name, product designation, batch number and application precaution labels.
MARISEAL AQUA PRIMER contains amines and epoxy resins. See information supplied by the manufacturer. Please study the Safety Data sheet. PROFESSIONAL USE ONLY.
15 +5 L
MARISEAL AQUA PRIMER is a transparent, rigid, two component epoxy primer. Water-based.
Used as a universal primer in waterproofing, sealing and floor coating applications on absorbent and non-absorbent surfaces.
Cures by reaction (cross linking) of the two components.