Solvent-based polyurethsne primer
MARISEAL 710 is a transparent, rigid, deep penetrating, one component, quick drying polyurethane primer.
Used as a primer in waterproofing and sealing applications on absorbent surfaces.
Cures by reaction with ground and air moisture.
The MARISEAL 710 is mainly used as a primer for polyurethane waterproofing coatings and polyurethane
joint sealants on absorbent surfaces like:
It can also be used as a primer on mineral-finished bitumen-felts as it bonds the mineral very efficient.
200 gr/m2 in one layer.
This coverage is based on practical application by roller onto a smooth surface in optimum conditions. Factors like surface porosity, temperature, humidity, application method and finish required can alter consumption.
The MARISEAL 710 is supplied transparent
Technical DataPROPERTY RESULTS TEST METHOD Composition Polyurethane pre-polymer. Solvent based Adhesion to concrete >1,8 N/mm2
Careful surface preparation is essential for optimum finish and durability.
The surface needs to be clean, dry and sound, free of any contamination, which may harmfully affect the adhesion of the membrane. Maximum moisture content should not exceed 5%. Substrate compressive strength should be at least 25MPa, cohesive bond strength at least 1.5MPa. New concrete structures need to dry for at least 28 days. Old, loose coatings, dirt, fats, oils, organic substances and dust need to be removed by a grinding machine. Possible surface irregularities need to be smoothened. Any loose surface pieces and grinding dust need to be thoroughly removed.
WARNING: Do not wash surface with water!
WARNING: Do not use a metal-ball blasting machine to grind the surface, because the heavy metal-ball impacts destroy the cohesion of the concrete surface and lower its stability.
For best results, the temperature during application and cure should be between 5oC and 35OC. Low temperatures retard cure, while high temperature speed up curing. High humidity may affect the final finish.
Apply the MARISEAL 710 by roller or brush, until the surface is covered. You can use airless spray allowing a considerable saving of manpower.
After 2-3 hours (not later than 4 hours) and while the primer is still a bit tacky, apply the polyurethane coating or the polyurethane joint sealant.
RECOMMENDATION: If the surface is very brittle, like lightweight concrete or porous cement screed, apply two layers of the MARISEAL 710.
MARISEAL 710 is supplied in 17 kg, 10 kg, 5 kg and 1kg pails. Pails should be stored in dry and cool rooms for up to 9months. Protect the material against moisture and direct sunlight. Storage temperature: 5-30C. Products should remain in their original, unopened containers, bearing the manufacturers name, product designation, batch number and application precaution labels.
MARISEAL 710 contains isocyanates. See information supplied by the manufacturer. Flammable. Please study the Safety Datasheet. PROFESSIONAL USE ONLY
Mariseal 710 is a solvent-based, transparent, semi-rigid, deep-penetrating, one component polyurethane primer. that cures by reaction with ground and air moisture
5L – 19cm x 19cm x 20cm
20L – 28cm x 28cm x 36cm
200-250gm per sq m
No of Coats:
1 coat application