Advantages

• Simple application.
• When applied forms seamless membrane without joints.
• Resistant to water.
• Resistant to frost.
• Provides excellent crack-bridging properties.
• Provides excellent thermal resistance
• Maintains its mechanical properties over a temperature span of-40C to +90C.
• Provides excellent adhesion to almost any type of surface.
• Resistant to domestic chemicals.
• Even if the membrane gets mechanically damaged, it can be easily repaired locally within minutes.
• Does not need the use of open flames (torch) during application
• Positive feedback worldwide.

Uses

The MARISEAL® 670 is used for:

• Waterproofing of Foundations
• Waterproofing of Retaining Walls
• Under-tile Waterproofing in Bathrooms, Kitchens,Balconies, Terraces, Roofs, etc

Consumption

1,5 kg/m2 applied in two or three layers.
This coverage is based on application by roller onto a smooth surface in optimum conditions. Factors like surface porosity, temperature and application method can alter consumption.

Colors

The MARISEAL® 670 is supplied in black.

Technical data

PROPERTY RESULTS TEST METHOD Elongation at Break > 650 % ASTM D 412 / DIN 52455 Tensile Strength > 4,5 N/ mm2 ASTM D 412 / DIN 52455

E-Modulus ~1,0 N/ mm2 ASTM D 412 / DIN 52455 Tear Resistance >15 N/ mm ASTM D 624 Puncture Resistance >150 N ASTM E 154 Resistance to Hydrostatic pressure No Leak @ 3 bar (30 m water column) DIN 16726 Adhesion to concrete >1,0 N/mm2 ASTM D 903 Hardness (Shore A Scale) 35 ASTM D 2240 (15”) Thermal Resistance (80C for 100 days) Passed – No significant changes EOTA TR-011 Hydrolysis (5% KOH, 7days cycle) No significant elastomeric change Inhouse Lab Service Temperature -40C to +90C Inhouse Lab Max. Temperature short time (15min shock) 250C Inhouse Lab Tack Free Time 5 hours Conditions: 20C, 50% RH Light Pedestrian Traffic Time 24 – 48 hours Final Curing time 7 days Chemical Properties Good resistance against acidic and alkali solutions (5%), detergents, seawater and oils.

Application

Surface Preparation

Careful surface preparation is essential for optimum finish and durability.
The surface needs to be clean, dry and sound, free of any contamination, which may harmfully affect the adhesion of the membrane. Maximum moisture content should not exceed 5%. Substrate compressive strength should be at least 25MPa, cohesive bond strength at least 1.5MPa. New concrete structures need to dry for at least 28 days. Old loose coatings, dirt, fats, oils, organic substances and dust need to be removed by a grinding machine. Possible surface irregularities need to be smoothened. Any loose surface pieces and grinding dust need to be thoroughly removed.
WARNING: Do not wash surface with water!

Repair of cracks and joints:

The careful sealing of existing cracks and joints before the application is extremely important for long lasting waterproofing results.

• Clean concrete cracks and hairline cracks, of dust, residue or other contamination. Prime locally with the MARISEAL 710 Primer and allow 2-3 hours to dry. Fill all prepared cracks with MARIFLEX® PU 30 sealant. Then apply a layer of MARISEAL 670,200mm wide centered over all cracks and while wet, cover with a correct cut stripe of the MARISEAL® Fabric. Press it to soak. Then saturate the MARISEAL® Fabric with enough MARISEAL 670, until it is fully covered. Allow 12 hours to cure.
• Clean concrete expansion joints and control joints of dust, residue or other contamination. Widen and deepen joints (cut open) if necessary. The prepared movement joint should have a depth of 10-15 mm. The width:depth ratio of the movement joint should be at a rate of approx. 2:1. Apply some MARIFLEX® PU 30 Joint-Sealant on the bottom of the joint only. Then with a brush, apply a stripe layer of MARISEAL® 670, 200mm wide centered over and inside the joint. Place the MARISEAL® Fabric over the wet coating and with a suitable tool, press it deep inside the joint, until it is soaked and the joint is fully covered from the inside. Then fully saturate the fabric with enough MARISEAL® 670. Then place a polyethylene cord of the correct dimensions inside the joint and press it deep inside onto the saturated fabric. Fill the remaining free space of the joint with MARIFLEX® PU 30 sealant. Do not cover. Allow 12- 18 hours to cure. The careful sealing of existing cracks and joints before the application is extremely important for long lasting waterproofing results.

Priming

On sound, high quality concrete surfaces no primer is necessary.
Prime very absorbent and brittle concrete or brittle cement screed surfaces with MARISEAL 710 or with MARISEAL AQUA
PRIMER. Prime non-absorbent surfaces like metal, ceramic tiles and old coatings with MARISEAL AQUA PRIMER. Allow the primer to cure according its technical instruction.

Waterproofing membrane

Stir well with electric drill mixer before using, for at least 2-3 minutes. Apply the MARISEAL 670 onto the surface by roller or brush, until all surface is covered. After 8-24 hours, apply another layer of the MARISEAL 670.
For demanding applications, apply a third layer of the MARISEAL 670.

Reinforce always with the MARISEAL® Fabric at problem areas, like wall-floor connections, 90o angles, chimneys, pipes, waterspouts (siphon), etc. In order to do that, apply on the still wet MARISEAL® 670 a correct cut piece of MARISEAL® Fabric, press it to soak, and saturate again with enough MARISEAL® 670. For detailed instructions with the MARISEAL® Fabric, contact our R+D department. If the MARISEAL 670 is to be covered with ceramic tiles, fully saturate with oven-dry silica sand (corn-size 0,4-0,8mm) the last layer while still wet. This saturation will create an adhesion bridge to the tile adhesive that will follow.

For best results, the temperature during application and cure should be between 5C and 35C. Low temperatures retard cure while high temperature speed up curing. High humidity may affect the final finish.
WARNING: The MARISEAL® 670 is slippery when wet. In order to avoid slipperiness, sprinkle suitable aggregates onto the still wet coating to create an anti-slip surface. Please contact our R+D Dept. for more details.

Protection /Thermoinsulation on Foundations/Retaining Walls

Protect the cured MARISEAL®670, with a drainage board before backfilling.
If an additional (optional) Thermoinsulation is required, place a insulation board (XPS, EPS, PUR, PIR, etc) on the cured MARISEAL 670. Following to that place the protective drainage board.

Packaging

MARISEAL® 670 is supplied in 25kg, 6kg and 1kg metal pails. Pails should be stored in dry and cool rooms for up to 9 months. Protect the material against moisture and direct sunlight. Storage temperature: 5-30C. Products should remain in their original, unopened containers, bearing the manufacturers name, product designation, batch number and application precaution labels.

Safety measures

MARISEAL 670 contains isocyanates. See information supplied by the manufacturer. Please study the Safety Data sheet.
PROFESSIONAL USE ONLY